T91 e phahameng khatello ea tšepe phala tiiso ea boleng
T91 steel ke mofuta o mocha oa tšepe e sa keneleng mocheso ea martensitic e entsoeng ke laboratori ea American National elephant ridge le Metallurgical Materials Laboratory ea k'hamphani ea boenjiniere ea ho chesa mollo ea Amerika. Motheong oa tšepe ea 9Cr1MoV, e fokotsa khabone, e beha meeli ea sebabole le phosphorus ka thata, 'me e eketsa palo e nyane ea vanadium le niobium bakeng sa alloying.
Sehlopha sa tšepe sa T91 seamless steel pipe e tsamaellanang le tšepe ea T91 ke x10crmovnnb91 Jeremane, hcm95 Japane le tuz10cdvnb0901 Fora.
Likahare tsa Element
S ≤0.01
Si 0.20-0.50
Cr 8.00-9.50
Mo 0.85-1.05
V 0.18-0,25
Nb 0.06-0.10
N 0.03-0.07
Ke ≤0.40
Ntho e 'ngoe le e' ngoe ea alloy ho T91 Steel e bapala karolo ea ho matlafatsa tharollo e tiileng, ho matlafatsa ho hasana le ho ntlafatsa khanyetso ea oxidation le ho hanyetsa kutu ea tšepe. Tlhahlobo e khethehileng ke e latelang.
①Carbon ke ntho e hlakileng ka ho fetisisa ea ho matlafatsa tharollo ka tšepe. Ka ho eketseha ha carbon content, matla a nakoana a tšepe a eketseha 'me polasetiki le ho tiea hoa fokotseha. Bakeng sa tšepe ea martensitic joalo ka T91, keketseho ea khabone e tla potlakisa spheroidization le aggregation ea carbide, ho potlakisa phetiso ea likarolo tsa alloy le ho fokotsa ho cheseha, ho hanyetsa kutu le khanyetso ea oxidation ea tšepe. Ka hona, tšepe e manganga mocheso ka kakaretso e batla ho fokotsa khabone, leha ho le joalo, haeba khabone e le tlase haholo, matla a tšepe a tla fokotseha. Ha ho bapisoa le tšepe ea 12Cr1MoV, carbon content ea T91 steel e fokotseha ka 20%, e khethiloeng ka ho hlahloba ka ho feletseng tšusumetso ea lintlha tse ka holimo.
②T91 tšepe e na le trace nitrogen, 'me karolo ea naetrojene e bonahala ka likarolo tse peli. Ka lehlakoreng le leng, e bapala karolo ea ho matlafatsa tharollo e tiileng. Ho qhibiliha ha naetrojene ka tšepe mochesong oa kamore e nyane haholo. Ts'ebetsong ea ho futhumatsa mocheso le kalafo ea mocheso oa weld, tharollo e tiileng ea VN le ts'ebetso ea pula e tla etsahala ka tatellano sebakeng se amehileng sa mocheso oa weld oa T91 Steel: sebopeho sa austenitic se thehiloeng sebakeng se amehileng ke mocheso nakong ea ho futhumatsa ha tjheseletsa se eketsa bongata ba naetrojene ka lebaka la ho qhibiliha ha VN, 'me joale tekanyo ea supersaturation mohahong o tloaelehileng oa mocheso oa eketseha, Ka mor'a phekolo ea mocheso oa poso ea weld, ho na le pula e ntle ea VN, e leng ho eketsang botsitso ba microstructure le ho ntlafatsa matla a tšoarellang a sebaka se amehileng ke mocheso. Ka lehlakoreng le leng, tšepe ea T91 e boetse e na le palo e nyane ea A1. Nitrogen e ka etsa A1N ka eona. A1N e qhibiliha ka har'a matrix ha feela e le ka holimo ho 1100 ℃ 'me e theoha hape ka mocheso o tlaase, o ka bapalang phello e ntle ea ho hasana.
③Ho eketsa chromium haholo-holo ho ntlafatsa khanyetso ea oxidation le khanyetso ea kutu ea tšepe e sa keneleng mocheso. Ha litaba tsa chromium li le ka tlase ho 5%, e qala ho oxidize ka matla ho 600 ℃, athe ha chromium e fihla ho 5%, e na le khanyetso e ntle ea oxidation. 12Cr1MoV tšepe e na le khanyetso e ntle ea oxidation ka tlase ho 580 ℃, 'me botebo ba kutu ke 0.05 mm / A. ho 600 ℃, ts'ebetso e qala ho senyeha, 'me botebo ba kutu ke 0.13 mm / A. Likahare tsa chromium tsa T91 li ka eketsoa ho isa ho hoo e ka bang 9% le mocheso oa tšebeletso o ka fihla ho 650 ℃. Mohato o ka sehloohong ke ho qhala chromium e eketsehileng ka matrix.
④Vanadium le niobium ke likarolo tse matla tsa ho etsa carbide. Ka mor'a ho phaella moo, ba ka etsa li-carbides tse ntle le tse tsitsitseng tse nang le carbon, tse nang le phello e matla ea ho hasana.
⑤ Molybdenum e eketsoa haholo ho ntlafatsa matla a mocheso a tšepe le ho bapala karolo ea ho matlafatsa tharollo e tiileng.
Phekolo ea ho qetela ea mocheso oa T91 e tloaelehile + mocheso o phahameng oa mocheso. Mocheso o tloaelehileng ke 1040 ℃, nako ea ho tšoara ha e ka tlase ho metsotso e 10, mocheso oa mocheso ke 730 ~ 780 ℃, 'me nako ea ho tšoara ha e ka tlase ho 1 h. The microstructure ka mor'a phekolo ea ho qetela ea mocheso ke tempered martensite.
Matla a tsitsitseng a tšepe ea T91 ka mocheso oa kamore ≥ 585 MPa, ho fana ka matla ka mocheso oa kamore ≥ 415 MPa, boima ≤ 250 Hb, elongation (sampole e tloaelehileng e chitja e nang le sebaka sa 50 mm gauge) ≥ 20%, boleng bo amohelehang ba khatello ea kelello [ σ] 650 ℄ 30 MPa.
Ho ea ka mokhoa o lekanang le oa khabone o khothaletsoang ke mokhatlo oa machaba oa ho cheselletsa, khabone e lekanang le T91 ke
Hoa hlokomeleha hore T91 e na le ts'ebetso e fokolang ea weldability.
T91 tšepe e na le tšekamelo e kholo ea ho phatloha ho batang 'me e na le tšekamelo ea ho lieha ho phatloha tlas'a maemo a itseng. Ka hona, lenonyeletso le cheselitsoeng le tlameha ho halefa nakong ea lihora tse 24 kamora ho cheselletsa. The microstructure ea T91 ka mor'a hore tjheseletsa ke poleiti le hlobolisa martensite, e ka fetoloang martensite e halefileng ka mor'a ho halefa, 'me thepa ea eona e phahametse poleiti le ho hlobolisa martensite. Ha mocheso oa mocheso o le tlase, phello ea mocheso ha e totobetse, 'me tšepe ea weld e bonolo ho tsofala le ho phunyeha; Haeba mocheso oa mocheso o phahame haholo (o fetang mohala oa AC1), lenonyeletso le ka 'na la tiisetsoa hape 'me la thatafala hape ka mokhoa o latelang oa ho pholile. Ka nako e ts'oanang, joalo ka ha ho boletsoe pejana pampiring ena, tšusumetso ea lera le nolofatsang lenonyeletso e lokela ho nahanoa ka boikemisetso ba mocheso oa mocheso. Ka kakaretso, mocheso oa mocheso oa T91 ke 730 ~ 780 ℃.
Nako ea mocheso e tsitsitseng ea T91 ka mor'a ho cheselletsa e ke ke ea e-ba ka tlase ho 1 h, e le ho netefatsa phetoho e feletseng ea sebopeho sa eona hore e be martensite e futhumetseng.
E le ho fokotsa khatello ea kelello e setseng ea T91 e entsoeng ka tšepe e entsoeng ka tšepe, sekhahla sa ho pholisa se tlameha ho laoloa ka tlase ho 5 ℃ / min. Mokhoa oa ho cheselletsa tšepe oa T91 o ka bontšoa setšoantšong sa 3.
Preheat 200 ~ 250 ℃; ② Welding, interlayer mocheso 200 ~ 300 ℃; ③ Ho pholile ka mor'a ho cheselletsa, ka lebelo la 80 ~ 100 ℃ / h; ④ 100 ~ 150 ℃ bakeng sa 1 h; ⑤ Ho futhumatsa ho 730 ~ 780 ℃ bakeng sa 1 h; ⑥ Fola ka sekhahla se seng ho feta 5 ℃ / min.
T91 Steel e itšetlehile ka molao-motheo oa ho kopanya, haholo-holo ho eketsa palo e nyenyane ea likarolo tse kang niobium le vanadium. Matla a eona a mocheso o phahameng le khanyetso ea oxidation e ntlafalitsoe haholo ha e bapisoa le tšepe ea 12 cr1mov, empa ts'ebetso ea eona ea tjheseletsa e fokola.
Teko ea pin e bontša hore tšepe ea T91 e na le tšekamelo e kholo ea ho phatloha ho batang. Ho khetha preheating 200 ~ 250 ℃ le interlayer mocheso 200 ~ 300 ℃ ka ka katleho thibela ho peperana batang.
T91 e tlameha ho pholile ho 100 ~ 150 ℃ bakeng sa 1 hora pele ho phekolo ea mocheso oa weld; Mocheso oa mocheso oa 730 ~ 780 ℃, o tšoara nako e seng ka tlase ho 1 h.
Mokhoa o ka holimo oa ho cheseletsa o sebelisitsoe tšebetsong ea tlhahiso le tlhahiso ea li-boilers tsa 200 MW le 300 MW, ka liphello tse khotsofatsang le melemo e meholo ea moruo.